PROPERTIES & AVERAGE VALUES OF INJECTION MOLDED SPECIMENS RTP901 |
PERMANENCE
|
English |
|
SI Metric |
|
ASTM
TEST |
|
Primary Additive |
10 % |
|
10 % |
|
|
Specific Gravity |
1.30 |
|
1.30 |
|
D 792 |
Molding Shrinkage |
|
1/8 in (3.2 mm) section |
0.0050 in/in |
|
0.50 % |
|
D 955 |
MECHANICAL
|
|
Impact Strength, Izod |
|
notched 1/8 in (3.2 mm) section |
1.2 ft-lbs/in |
|
64 J/m |
|
D 256 |
unnotched 1/8 in (3.2 mm) section |
13.0 ft-lbs/in |
|
694 J/m |
|
D 4812 |
Tensile Strength |
12000 psi |
|
83 MPa |
|
D 638 |
Tensile Elongation |
5.0 % |
|
5.0 % |
|
D 638 |
Tensile Modulus |
0.50 x 10^6 psi |
|
3448 MPa |
|
D 638 |
Flexural Strength |
19000 psi |
|
131 MPa |
|
D 790 |
Flexural Modulus |
0.50 x 10^6 psi |
|
3448 MPa |
|
D 790 |
Hardness |
|
Rockwell, R |
122 |
|
122 |
|
D 785 |
ELECTRICAL
|
|
Dielectric Strength, S/T, in oil |
430 VPM |
|
16.9 kV/mm |
|
D 149 |
Dielectric Constant, 1 MHz, Dry |
3.5 |
|
3.5 |
|
D 150 |
Dissipation Factor, 1 MHz, Dry |
0.0050 |
|
0.0050 |
|
D 150 |
Arc Resistance |
100 s |
|
100 s |
|
D 495 |
Volume Resistivity |
> 1E12 ohm.cm |
|
> 1E12 ohm.cm |
|
D 257 |
THERMAL
|
|
Deflection Temperature |
|
@ 264 psi (1820 kPa) |
350 °F |
|
177 °C |
|
D 648 |
@ 66 psi (455 kPa) |
360 °F |
|
182 °C |
|
D 648 |
Ignition Resistance* |
|
Flammability** |
VTM-2 @ 1/16 in |
|
VTM-2 @ 1.5 mm |
|
D 4804 |
Coefficient of Linear Thermal Expansion |
|
Flow Direction |
2.1 x 10-5/°F |
|
3.8 x 10-5/°C |
|
E 831 |
Thermal Conductivity |
|
Through-plane |
1.90 (BTU.in)/(hr.ft2.°F) |
|
0.27 W/(m.K) |
|
E 1530 |
PROPERTY NOTES |
|
English |
|
SI Metric |
|
|
|
|