性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
比重 |
|
ASTM D792 |
1.24 |
g/cm3 |
吸水率 |
|
ASTM D570 |
0.30 |
% |
熔体质量流动速率 |
|
ASTM D1238 |
6.5 |
g/10min |
成型收缩率 |
|
ASTM D955 |
0.007 |
% |
拉伸强度 |
|
ASTM D638 |
70.3 |
MPa |
拉伸模量 |
|
ASTM D638 |
2480 |
MPa |
拉伸断裂拉长率 |
|
ASTM D638 |
50-100 |
% |
弯曲强度 |
|
ASTM D790 |
106.2 |
MPa |
弯曲模量 |
|
ASTM D790 |
2690 |
MPa |
拉伸冲击强度 |
|
ASTM D1822 |
420 |
KJ/m2 |
IZOD缺口冲击强度 |
|
ASTM D256 |
6.9 |
KJ/m2 |
绝缘强度 |
|
ASTM D149 |
17 |
kV/mm |
介电常数 |
60 Hz |
ASTM D150 |
3.03 |
|
介电常数 |
1000 Hz |
ASTM D150 |
3.04 |
|
介电常数 |
1000000 Hz |
ASTM D150 |
3.02 |
|
介质损耗因数 |
60 Hz |
ASTM D150 |
0.0007 |
|
介质损耗因数 |
1000 Hz |
ASTM D150 |
0.0010 |
|
介质损耗因数 |
1000000 Hz |
ASTM D150 |
0.0060 |
|
体积电阻 |
|
ASTM D257 |
3×1016 |
Ω·cm |
热变形温度 |
1.82MPa |
ASTM D648 |
174 |
℃ |
膨胀系数 |
|
ASTM D696 |
56 |
ppm/°C |
|