Material Notes:

NORYL GTX830 a 30% glass reinforced grade which offers an excellent combination of chemical/heat resistance in combination with stiffness.

Vendors:

No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.

Physical Properties

Metric

English

Comments

Density 

1.32 g/cc

0.0477 lb/in3

ISO 1183

Moisture Absorption 

1.09 %

1.09 %

23°C / 50% RH; ISO 62

Water Absorption at Saturation 

3.1 %

3.1 %

ISO 62

Linear Mold Shrinkage, Flow 

0.0020 - 0.0030 cm/cm
@Thickness 3.20 mm

0.0020 - 0.0030 in/in
@Thickness 0.126 in

SABIC Method

Linear Mold Shrinkage, Transverse 

0.0080 - 0.010 cm/cm
@Thickness 3.20 mm

0.0080 - 0.010 in/in
@Thickness 0.126 in

SABIC Method

Melt Index of Compound 

7.0 g/10 min
@Load 5.00 kg,
Temperature 280 °C

7.0 g/10 min
@Load 11.0 lb,
Temperature 536 °F

MVR [cm^3/10 min]; ISO 1133

Mechanical Properties

Metric

English

Comments

Hardness, H358/30 

110 MPa

16000 psi

ISO 2039-1

Tensile Strength at Break 

110 MPa

16000 psi

5 mm/min; ISO 527

Elongation at Break 

2.5 %

2.5 %

5 mm/min; ISO 527

Tensile Modulus 

7.30 GPa

1060 ksi

1 mm/min; ISO 527

Flexural Strength 

170 MPa

24700 psi

break, 2 mm/min; ISO 178

Flexural Modulus 

6.20 GPa

899 ksi

2 mm/min; ISO 178

Izod Impact, Unnotched (ISO) 

45.0 kJ/m2

21.4 ft-lb/in2

80*10*4; ISO 180/1U

45.0 kJ/m2
@Temperature -30.0 °C

21.4 ft-lb/in2
@Temperature -22.0 °F

80*10*4; ISO 180/1U

Charpy Impact Unnotched 

6.00 J/cm2

28.6 ft-lb/in2

Edgew 80*10*4 sp=62mm; ISO 179/1eU

4.00 J/cm2
@Temperature -30.0 °C

19.0 ft-lb/in2
@Temperature -22.0 °F

Edgew 80*10*4 sp=62mm; ISO 179/1eU

Charpy Impact, Notched 

0.700 J/cm2

3.33 ft-lb/in2

ISO 179/2C

0.700 J/cm2
@Temperature -20.0 °C

3.33 ft-lb/in2
@Temperature -4.00 °F

ISO 179/2C

Thermal Properties

Metric

English

Comments

CTE, linear, Parallel to Flow 

20.0 μm/m-°C
@Temperature 23.0 - 60.0 °C

11.1 μin/in-°F
@Temperature 73.4 - 140 °F

ISO 11359-2

CTE, linear, Transverse to Flow 

80.0 μm/m-°C
@Temperature 23.0 - 60.0 °C

44.4 μin/in-°F
@Temperature 73.4 - 140 °F

ISO 11359-2

Thermal Conductivity 

0.260 W/m-K

1.80 BTU-in/hr-ft2-°F

ISO 8302

Vicat Softening Point 

220 °C

428 °F

Rate B/120; ISO 306

220 °C

428 °F

Rate B/50; ISO 306

UL RTI, Electrical 

120 °C

248 °F

UL 746B

UL RTI, Mechanical with Impact 

90.0 °C

194 °F

UL 746B

UL RTI, Mechanical without Impact 

125 °C

257 °F

UL 746B

Flammability, UL94  

HB
@Thickness 1.50 mm

HB
@Thickness 0.0591 in

UL 94

HB
@Thickness 3.00 mm

HB
@Thickness 0.118 in

UL 94

Oxygen Index 

29 %

29 %

ISO 4589