TYPICAL PROPERTIES (1) |
MECHANICAL |
Value |
Unit |
Standard |
Tensile Stress, yld, Type I, 50 mm/min |
640 |
kgf/cm2 |
ASTM D 638 |
Tensile Stress, brk, Type I, 50 mm/min |
520 |
kgf/cm2 |
ASTM D 638 |
Tensile Strain, yld, Type I, 50 mm/min |
5.1 |
% |
ASTM D 638 |
Tensile Strain, brk, Type I, 50 mm/min |
29.3 |
% |
ASTM D 638 |
Tensile Modulus, 5 mm/min |
22000 |
kgf/cm2 |
ASTM D 638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span |
1050 |
kgf/cm2 |
ASTM D 790 |
Flexural Modulus, 1.3 mm/min, 50 mm span |
26800 |
kgf/cm2 |
ASTM D 790 |
Tensile Stress, yield, 50 mm/min |
64 |
MPa |
ISO 527 |
Tensile Stress, break, 50 mm/min |
53 |
MPa |
ISO 527 |
Tensile Strain, yield, 50 mm/min |
4.9 |
% |
ISO 527 |
Tensile Strain, break, 50 mm/min |
20.7 |
% |
ISO 527 |
Tensile Modulus, 1 mm/min |
2900 |
MPa |
ISO 527 |
Flexural Stress, yield, 2 mm/min |
107 |
MPa |
ISO 178 |
Flexural Modulus, 2 mm/min |
2620 |
MPa |
ISO 178 |
IMPACT |
Value |
Unit |
Standard |
Izod Impact, notched, 23°C |
17 |
cm-kgf/cm |
ASTM D 256 |
Izod Impact, notched, -30°C |
9 |
cm-kgf/cm |
ASTM D 256 |
Instrumented Impact Total Energy, 23°C |
348 |
cm-kgf |
ASTM D 3763 |
Izod Impact, notched 80*10*4 +23°C |
15 |
kJ/m2 |
ISO 180/1A |
Izod Impact, notched 80*10*4 -30°C |
7 |
kJ/m2 |
ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm |
15 |
kJ/m2 |
ISO 179/1eA |
THERMAL |
Value |
Unit |
Standard |
Vicat Softening Temp, Rate B/50 |
136 |
°C |
ASTM D 1525 |
HDT, 1.82 MPa, 3.2mm, unannealed |
114 |
°C |
ASTM D 648 |
CTE, -40°C to 40°C, flow |
7.39E-05 |
1/°C |
ASTM E 831 |
CTE, -40°C to 40°C, xflow |
7.12E-05 |
1/°C |
ASTM E 831 |
CTE, -40°C to 40°C, flow |
7.12E-05 |
1/°C |
ISO 11359-2 |
CTE, -40°C to 40°C, xflow |
7.39E-05 |
1/°C |
ISO 11359-2 |
Vicat Softening Temp, Rate B/50 |
136 |
°C |
ISO 306 |
Vicat Softening Temp, Rate B/120 |
138 |
°C |
ISO 306 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm |
116 |
°C |
ISO 75/Af |
PHYSICAL |
Value |
Unit |
Standard |
Specific Gravity |
1.08 |
- |
ASTM D 792 |
Mold Shrinkage, flow, 3.2 mm (5) |
0.5 - 0.8 |
% |
SABIC Method |
Melt Flow Rate, 280°C/5.0 kgf |
9.5 |
g/10 min |
ASTM D 1238 |
Density |
1.08 |
g/cm3 |
ISO 1183 |
Water Absorption, (23°C/sat) |
0.25 |
% |
ISO 62 |
Moisture Absorption (23°C / 50% RH) |
0.05 |
% |
ISO 62 |
Melt Volume Rate, MVR at 280°C/5.0 kg |
9 |
cm3/10 min |
ISO 1133 |