TYPICAL PROPERTIES (1) |
MECHANICAL |
Value |
Unit |
Standard |
Tensile Stress, yld, Type I, 50 mm/min |
810 |
kgf/cm2 |
ASTM D 638 |
Tensile Stress, brk, Type I, 50 mm/min |
570 |
kgf/cm2 |
ASTM D 638 |
Tensile Strain, yld, Type I, 50 mm/min |
29 |
% |
ASTM D 638 |
Tensile Strain, brk, Type I, 50 mm/min |
5.2 |
% |
ASTM D 638 |
Tensile Modulus, 5 mm/min |
28300 |
kgf/cm2 |
ASTM D 638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span |
1270 |
kgf/cm2 |
ASTM D 790 |
Flexural Modulus, 1.3 mm/min, 50 mm span |
29900 |
kgf/cm2 |
ASTM D 790 |
Tensile Stress, yield, 50 mm/min |
79 |
MPa |
ISO 527 |
Tensile Stress, break, 50 mm/min |
72 |
MPa |
ISO 527 |
Tensile Strain, yield, 50 mm/min |
4.7 |
% |
ISO 527 |
Tensile Strain, break, 50 mm/min |
7.6 |
% |
ISO 527 |
Tensile Modulus, 1 mm/min |
3110 |
MPa |
ISO 527 |
Flexural Stress, yield, 2 mm/min |
123 |
MPa |
ISO 178 |
Flexural Modulus, 2 mm/min |
2970 |
MPa |
ISO 178 |
IMPACT |
Value |
Unit |
Standard |
Izod Impact, notched, 23°C |
3 |
cm-kgf/cm |
ASTM D 256 |
Izod Impact, notched, -30°C |
2 |
cm-kgf/cm |
ASTM D 256 |
Instrumented Impact Total Energy, 23°C |
94 |
cm-kgf |
ASTM D 3763 |
Izod Impact, notched 80*10*4 +23°C |
4 |
kJ/m2 |
ISO 180/1A |
Izod Impact, notched 80*10*4 -30°C |
3 |
kJ/m2 |
ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm |
3 |
kJ/m2 |
ISO 179/1eA |
THERMAL |
Value |
Unit |
Standard |
Vicat Softening Temp, Rate B/50 |
141 |
°C |
ASTM D 1525 |
HDT, 1.82 MPa, 3.2mm, unannealed |
122 |
°C |
ASTM D 648 |
CTE, -40°C to 40°C, flow |
7.9E-05 |
1/°C |
ASTM E 831 |
CTE, -40°C to 40°C, xflow |
8.E-05 |
1/°C |
ASTM E 831 |
CTE, -40°C to 40°C, flow |
7.9E-05 |
1/°C |
ISO 11359-2 |
CTE, -40°C to 40°C, xflow |
8.E-05 |
1/°C |
ISO 11359-2 |
Ball Pressure Test, 75°C +/- 2°C |
N/A |
- |
IEC 60695-10-2 |
Vicat Softening Temp, Rate B/50 |
141 |
°C |
ISO 306 |
Vicat Softening Temp, Rate B/120 |
142 |
°C |
ISO 306 |
|