RTP2099x61745G


PROPERTIES & AVERAGE VALUES OF INJECTION MOLDED SPECIMENS


PERMANENCE

English

 

SI Metric

 

ASTM
TEST

 

Primary Additive

30 %

 

30 %

 

 

Specific Gravity

1.48

 

1.48

 

 D 792


MECHANICAL

 

Impact Strength, Izod

 

    notched 1/8 in (3.2 mm) section

1.0 ft-lbs/in

 

53 J/m

 

 D 256

    unnotched 1/8 in (3.2 mm) section

6.0 ft-lbs/in

 

320 J/m

 

 D 4812

Tensile Strength

16000 psi

 

110 MPa

 

 D 638

Tensile Elongation

1.5 %

 

1.5 %

 

 D 638

Tensile Modulus

1.48 x 10^6 psi

 

10205 MPa

 

 D 638

Flexural Strength

21000 psi

 

145 MPa

 

 D 790

Flexural Modulus

1.63 x 10^6 psi

 

11239 MPa

 

 D 790


THERMAL

 

Deflection Temperature

 

    @ 264 psi (1820 kPa)

 

 

210 °C

 

 D 648

    @ 66 psi (455 kPa)

 

 

218C

 

 D 648

 

PROPERTY NOTES

 

Data herein is typical and not to be construed as specifications.
Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.


GENERAL PROCESSING FOR INJECTION MOLDING

 

English

 

SI Metric

 

 

 

Injection Pressure

8000 - 15000 psi

 

55 - 103 MPa

 

 

Melt Temperature

340 - 380 °F

 

171 - 193 °C

 

 

Mold Temperature

180 - 220 °F

 

82 - 104 °C

 

 

Drying

2 - 6 hrs @ 130 °F

 

2 - 6 hrs @ 54 °C

 

 

Moisture Content

0.02 %

 

0.02 %

 

 

Dew Point

-40 °F

 

-40 °C

 

 