Physical Properties |
Metric |
English |
Comments |
Specific Gravity |
1.34 g/cc |
1.34 g/cc |
ASTM D792 |
Melt Flow |
11.3 g/10 min
@Load 6.60 kg,
Temperature 337 °C |
11.3 g/10 min
@Load 14.6 lb,
Temperature 639 °F |
ASTM D1238 |
Mechanical Properties |
Metric |
English |
Comments |
Tensile Strength at Break |
115 MPa |
16700 psi |
Type I, 5 mm/min; ASTM D638 |
Tensile Strength, Yield |
114 MPa |
16500 psi |
Type I, 5 mm/min; ASTM D638 |
Elongation at Break |
6.00 % |
6.00 % |
Type I, 5 mm/min; ASTM D638 |
Tensile Modulus |
4.61 GPa |
669 ksi |
5 mm/min; ASTM D638 |
Flexural Strength |
199 MPa |
28900 psi |
brk, 2.6 mm/min, 100 mm span; ASTM D790 |
Flexural Modulus |
5.24 GPa |
760 ksi |
2.6 mm/min, 100 mm span; ASTM D790 |
Izod Impact, Notched |
0.480 J/cm |
0.899 ft-lb/in |
ASTM D256 |
|
4.00 J/cm
@Thickness 3.20 mm |
7.49 ft-lb/in
@Thickness 0.126 in |
ASTM D256 |
Electrical Properties |
Metric |
English |
Comments |
Arc Resistance |
60.0 - 120 sec |
60.0 - 120 sec |
Tungsten; ASTM D495 |
Comparative Tracking Index |
100 - 175 V |
100 - 175 V |
UL 746A |
Hot Wire Ignition, HWI |
60.0 - 120 sec |
60.0 - 120 sec |
UL 746A |
High Amp Arc Ignition, HAI |
0.000 - 15.0 arcs |
0.000 - 15.0 arcs |
UL 746A |
High Voltage Arc-Tracking Rate, HVTR |
25.4 - 80.0 mm/min |
1.00 - 3.15 in/min |
UL 746A |
Thermal Properties |
Metric |
English |
Comments |
Deflection Temperature at 1.8 MPa (264 psi) |
207 °C
@Thickness 6.40 mm |
405 °F
@Thickness 0.252 in |
unannealed; ASTM D648 |
UL RTI, Electrical |
170 °C |
338 °F |
UL 746B |
UL RTI, Mechanical with Impact |
170 °C |
338 °F |
UL 746B |
UL RTI, Mechanical without Impact |
170 °C |
338 °F |
UL 746B |
Flammability, UL94 |
V-0
@Thickness 0.400 mm |
V-0
@Thickness 0.0157 in |
UL 94 |
|
5VA
@Thickness 1.90 mm |
5VA
@Thickness 0.0748 in |
UL 94 |