性能项目
| 试验条件[状态]
| 测试方法
| 测试数据
| 数据单位 |
物理性能
| 比 重
| 黑 色
| ASTM D-792
| 1.62
| |
| 模缩率
| 流向1.6mm
| ASTM D-955
| -0.1
| % |
| 泰伯摩擦
|
| ASTM D-1044
| 63
| mg |
| 模缩率
| 流向3.2mm
| ASTM D-955
| 0
| % |
| 模缩率
| 横向1.6mm
| ASTM D-955
| 0.9
| % |
机械性能
| 弯曲模量
| 23℃,1.6mm
| ASTM D-790
| 14000
| MPa |
| 无缺口冲击强度
| 23℃,3.2mm
| ASTM D-4812
| 555,20%NB
| j/m |
| 弯曲模量
| 23℃,0.8mm
| ASTM D-790
| 18000
| MPa |
| 冲击下机械性能
|
| UL 746B
| 210
| oC |
| 拉伸模量
| 23℃,3.2mm
| ASTM D-638
| 18000
| MPa |
| 弯曲模量
| 23℃,3.2mm
| ASTM D-790
| 13100
| MPa |
| 拉伸强度
| 23℃,1.6mm
| ASTM D-638
| 173
| MPa |
| IZOD冲击强度
| 23℃,0.8mm
| ASTM D-256
| 400,40%NB
| j/m |
| 无缺口冲击强度
| 23℃,1.6mm
| ASTM D-4812
| 840
| j/m |
| 模缩率
| 横向3.2mm
| ASTM D-955
| 0.8
| % |
| 弯曲强度
| 23℃,3.2mm
| ASTM D-790
| 183
| MPa |
| 弯曲强度
| 23℃,0.8mm
| ASTM D-790
| 215
| MPa |
| 压缩强度
| 3.2mm
| ASTM D-695
| 89
| MPa |
| 拉伸模量
| 23℃,1.6mm
| ASTM D-638
| 19306
| MPa |
| 断裂伸长率
| 23℃,3.2mm
| ASTM D-638
| 1.7
| % |
| 弯曲疲劳
| 3.2mm，69MPa
| ASTM D-671
| 2667
| cycle |
| 断裂伸长率
| 23℃,1.6mm
| ASTM D-638
| 1.6
| % |
| IZOD冲击强度
| 23℃,3.2mm
| ASTM D-256
| 225
| j/m |
| 洛氏硬度
| Scale M
| ASTM D-785
| 63
| |
| 拉伸强度
| 23℃,3.2mm
| ASTM D-638
| 150
| MPa |
| 弯曲强度
| 23℃,1.6mm
| ASTM D-790
| 192
| MPa |
| IZOD冲击强度
| 23℃,1.6mm
| ASTM D-256
| 170
| j/m |
电气性能
| 介电强度
| 1.6mm逐步
| ASTM D-149
| 31
| KV/mm |
| 介电常数
| 23℃,0.8mm,1×109Hz
| ASTM D-2520B
| 4.4
| |
| 介电常数
| 23℃,3.2mm,1×103Hz
| ASTM D-150
| 4.3
| |
| 损耗因素
| 23℃,1.6mm,1×109Hz
| ASTM D-2520B
| 0.004
| |
| 损耗因素
| 23℃,3.2mm,1×106Hz
| ASTM D-150
| 0.029
| |
| 损耗因素
| 23℃,3.2mm,1×109Hz
| ASTM D-2520B
| 0.004
| |
| 介电强度
| 23℃,1.6mm短时间
| ASTM D-149
| 35
| KV/mm |
| 介电强度
| 23℃,3.2mm短时间
| ASTM D-149
| ＞28
| KV/mm |
| 介电常数
| 23℃,3.2mm,1×106Hz
| ASTM D-150
| 3.8
| |
| 体积电阻率
|
| ASTM D-257
| 1×1016
| Ω.cm |
| 损耗因素
| 23℃,3.2mm,1×103Hz
| ASTM D-150
| 0.013
| |
| 介电常数
| 23℃,3.2mm,1×109Hz
| ASTM D-2520B
| 4.3
| |
| 介电常数
| 23℃,0.8mm,1×103Hz
| ASTM D-150
| 3.9
| |
| 损耗因素
| 23℃,0.8mm,1×103Hz
| ASTM D-150
| 0.013
| |
| 损耗因素
| 23℃,0.8mm,1×106Hz
| ASTM D-150
| 0.029
| |
| 损耗因素
| 23℃,0.8mm,1×109Hz
| ASTM D-2520B
| 0.004
| |
| 表面电阻率
|
| ASTM D-257
| 1×1015
| Ω |
| 介电常数
| 23℃,0.8mm,1×106Hz
| ASTM D-150
| 3.5
| |
加工性能
| 熔解温度范围
| ℃
|
| 363～371
| |
| 模具温度范围
| ℃
|
| 30～95
| |
| 干燥时间（除湿干燥剂）
|
|
| 2
| h |
| 加工时水气含量
|
|
| ＜0.01
| % |
| 干燥温度
|
|
| 135
| ℃ |
热性能
| 熔 点
|
| ASTM D-3418
| 352
| oC |
| 导热性
|
| ASTM C-177
| 0.32
| W/m k |
| 玻璃转变温度
|
| ASTM D-3418
| 120
| oC |
| 热变形温度
|
| ASTM D-648
| 289
| oC |
| 相关温度指数
|
| UL 746B
| 240
| oC |
| 外推最终融温
|
| ASTM D-3418
| 360
| oC |
其它性能
| 厚度测试
|
| UL 94
| 0.75
| mm |
| 厚度比率
|
| UL 94
| V-0
| |
| 限制氧气指数
| 3.2mm
| ASTM D-2863
| 39
| % |
|